请教高手PLC 655是哪个国家生产的油漆，他的温度可耐500高温，而且为单组分，其颜色为橘红色，RAL2004哪位高人知道这种情可能吗，一般高温漆不都是铝粉漆吗，酚醛环氧也耐不到500℃

作者: masxyb1 时间: 2010-5-14 11:13
无机的油漆可以耐高温的！

作者: bts 时间: 2010-5-14 12:18
你新来的吧，有机硅耐500度很轻松啊

作者: chgdong213 时间: 2010-5-14 16:01

你新来的吧，有机硅耐500度很轻松啊
bts 发表于 2010-5-14 12:18

但是能做成橘红色吗?请核实再回答

作者: sonow 时间: 2010-5-14 18:54
不清楚涂料中的情况，但在硅橡胶中常用y型氧化铁作为抗氧化剂，表观上为红色

作者: ztflove 时间: 2010-5-17 16:33
你找样品500度烤一个小时试试

作者: liuxfei79 时间: 2010-5-31 21:55

PRODUCT DATA SHEET

Rev. 1/04.05

PLC 655 HT

HIGH TEMPERATURE COATING

DESCRIPTION

PLC 655 HT is a single component protective coating

for high temperature services. The coating will

withstand continuous high temperature exposure up to

500°C. It exhibits excellent outdoor weathering

properties and suitable for coastal and industrial

environment.

RECOMMENDED USES

PLC 655 HT is recommended for protection of

equipment exposed to high temperature like stacks,

boiler, heat exchanger hot piping, mufflers, exhaust,

furnace and etc. Generally used where temperature

exceeds 260°C. To further enhance the corrosion

protection properties, an inorganic zinc primer is

highly recommended before application of
PLC 655

HT.

LIMITATIONS

PLC 655 HT is not recommended for immersion

service and chemical exposure.

ADVANTAGES

•
Good abrasion resistance.

•
Temperature resistance up to 500°C

•
Withstand thermal shock from 500°C to 0°C

•
Adhesion – Excellent adhesion over steel.

•
Very good flexibility.

PHYSICAL DATA

Finish : Semi Gloss

Volume Solids
:
30 ± 1 %

No. of Components
:
One

Recommended

: 40 microns DFT per

Thickness

coat

Theoretical Coverage :
7.5m²/litre @ 40

microns DFT

No. of coats
: One to two coats

recommended

Drying Time

Touch dry
:
1 hour

Top coating
:
3 hours

Packing Size
:
5 litres & 20 litres

Temperature

:
Continuous 500°C

resistance (dry)

作者: liuxfei79 时间: 2010-5-31 21:56
日资企业，PLC Laboratory

作者: liuxfei79 时间: 2010-5-31 21:58
PLC Laboratory Sdn Bhd。 www.plc.com.my

作者: tank 时间: 2010-6-1 12:20

但是能做成橘红色吗?请核实再回答
chgdong213 发表于 2010-5-14 16:01

镉系颜料具有非常优异的耐温性，只不过含重金属。。

作者: alexander.yee 时间: 2010-6-2 17:04
不会是铬红吧~~~~